PA600 High Performance Flame Retardant Masterbatch (PA600)

Original
price: Negotiable
minimum:
Total supply:
Delivery term: The date of payment from buyers deliver within days
seat: Beijing
Validity to: Long-term effective
Last update: 2017-07-07 08:04
Browse the number: 85
inquiry
Company Profile
 
 
Product details

Suzhou Haixiang Plastic Chemical Co.,Ltd is one of the leading China pa600 high performance flame retardant masterbatch (pa600) manufacturers. With professional factory, we are able to produce universal, high performance, high cost performance, popular, steady, high capacity, and nice reputation pa600 high performance flame retardant masterbatch (pa600). If you are checking China distributor, China export and import, please feel free to contact us. And welcome to buy and purchase cheap and high-quality or wholesale pa600 high performance flame retardant masterbatch (pa600) from us.

Introduction

HXFR-PA600 consists of environment friendly and high temperature resistant flame retardant system of bromine and antimony, passed the evaluation of SGS, CTI etc. certification authority and comply with ROHS requirement. Advantage: good compatibility with PA66, low dosage, low cost, high UV-Resistance, non-blooming.

Application

Mainly used in power tools, parts, mechanical instrument, connecter, and connection bolt etc.

Index

Appearance

White granular

Content %

90

Solubility index g/min,  200℃10kg

29

Density  g/cm³

2.08

Water Content%≤

0.1

Recommended Dosage

16-18

Melting Temp  ℃≥

110





PA66 Extrusion process (Twin Screw Extruder)

Note: Vacuum when production; Recommended Screw L/D 1:36-40; Rotation speed should be not more than 320 rmp when production with PA66+GF.

Recommended Screw Combination Chart

52 machine (Thread Block total 40 pcs, Screw L/D1:36)

1

32/32



22

48/48

Vent

2

32/32


23

48/48

3

32/32


24

32/32


4

48/48


25

16L


5

48/48


26

60°/4/32


6

48/48


27

45°/5/48


7

64/64

Vacuum

28

45°/5/48


8

64/64

29

32/32


9

16L


30

90°/5/48


10

90°/5/48


31

45°/5/48


11

60°/4/32


32

45°/5/48


12

32/32


33

32/32


13

32/32


34

48/48


14

90°/5/48


35

48/48


15

60°/4/32


36

48/48


16

32/32


37

64/64


17

32/32


38

64/64


18

60°/4/32


39

64/64


19

45°/5/48


40

48/48A


20

32/32


.Feeding

21

32/32



Thread Block Model

Number

Total Length(mm)

16L

2

32

32/32

12

384

48/48

8

384

48/48A

1

48

64/64

5

320

45 °/5/48

5

240

60 °/4/32

4

132

90 °/5/48

3

144

Total

40

1684

Packing/Storage

25KG/bag: Transported as a common chemical and stored in dry and cool place, avoid direct sunlight

Appendix:Application examples

1. Formula:

Materials

Formula A

Formula B

PA66+GF30%

82


PA600

18


PA601



2. Technical Data:

Properties

Test Methods

Unit

Raw Materials  PA66+GF30%

Formula A

Formula B

Density

ASTM D-792

G/cm3³

1.43

1.53


Melt Index(200℃/5KG)

ASTM D-955

g/10min




Tensile strength

ASTM- D638

MPa

157

109


Elongation At Break

ASTM-D638

%

2.8

3.75


Flexural Strength

ASTM-D790

MPa

200.5

175.8


Flexural Modulus

ASTM-D790

MPa

6483.7

5880


Izod Impact Strength Notched (23℃)

ASTM-D256

KJ/m2

15.2

15.2


Flame Retardancy  3.2mm

UL94

--

Non flame retardant

V0


3. PA66 Injection Process

Drying condition: Drying at 70-75 deg C to 2-3 hours by desiccant dryers

Injection machine Temperature Setup

Heating Zone

Nozzle

Step 1

Step 2

Step 3

Temperature

260

265

260

250

Note:

1.All the application typical data above are just for reference, not an official warranty certificate.

2.Provide different design solutions according to requirement of customers.


Total0bar [View All]  Related Comments
 
more»Other products

[ Products search ] [ favorites ] [ Tell friends ] [ Print ] [ Close ]